Chemical and mechanical stability of air annealed cathodic arc evaporated CrAlON coatings
Fecha
2018Autor
Versión
Acceso abierto / Sarbide irekia
Tipo
Artículo / Artikulua
Versión
Versión aceptada / Onetsi den bertsioa
Identificador del proyecto
Impacto
|
10.1016/j.surfcoat.2018.07.081
Resumen
This study reports the synthesis and characterization of ternary Cr-Al-O and quaternary Cr-Al-O-N coatings deposited by cathodic arc physical vapour deposition, for various nitrogen and oxygen mass flow ratios during the growth process. The composition, microstructure, indentation hardness and modulus of the films have been characterized by scanning electron microscopy, electron probe micro-analy ...
[++]
This study reports the synthesis and characterization of ternary Cr-Al-O and quaternary Cr-Al-O-N coatings deposited by cathodic arc physical vapour deposition, for various nitrogen and oxygen mass flow ratios during the growth process. The composition, microstructure, indentation hardness and modulus of the films have been characterized by scanning electron microscopy, electron probe micro-analysis, X-ray diffraction, and nanoindentation techniques. The evolution of the microstructure and mechanical properties of the coatings after ambient air annealing from 800 °C up to 1100 °C have been investigated. As the oxygen to nitrogen mass flow increases, the as-deposited coatings exhibit lower hardness, higher roughness, lower crystallinity and a more marked columnar structure. At oxygen to nitrogen mass flow ratios bigger than 10/90, the coatings exhibit a stoichiometry of the type (CrAl)2+εO3−ε. Only the coatings with an oxygen to nitrogen mass flow ratio smaller than 10/90 retained nitrogen in their compositions. In all cases, the coatings developed a cubic fcc lattice structure. After annealing at 1100 °C the resulting microstructure showed a clear dependency upon the initial composition of the films. The evolution of the microstructure during the high temperature tests, as well as the analysis of the nanoindentation hardness, composition and thickness also provided valuable information about the combined effects of the thermal stability and the oxidation of the deposited coatings. [--]
Materias
CrAlON coatings,
Wear,
Cathodic arc evaporation,
Thermal stability
Editor
Elsevier
Publicado en
Surface and Coatings Technology, 2018, 351, 153-161
Departamento
Universidad Pública de Navarra. Departamento de Ingeniería /
Nafarroako Unibertsitate Publikoa. Ingeniaritza Saila /
Universidad Pública de Navarra/Nafarroako Unibertsitate Publikoa. Institute for Advanced Materials and Mathematics - INAMAT2
Versión del editor
Entidades Financiadoras
This work has been funded by the Spanish Ministry of Economy and Competitiveness through the project PROTEOX MAT2013-45391-P. The European Commission is also acknowledged through the FP7-FOFNMP project MICROFAST under contract Nr 608720. The Research Group of Surface Engineering and Nanostructured Materials in the Universidad Complutense de Madrid also acknowledges financial support of the Spanish MINECO (project MAT2015-65539-P).