Effect of Cu substitution on the magnetic and magnetic induction heating response of CdFe₂O₄ spinel ferrite
Fecha
2020Autor
Versión
Acceso abierto / Sarbide irekia
Tipo
Artículo / Artikulua
Versión
Versión aceptada / Onetsi den bertsioa
Identificador del proyecto
Impacto
|
10.1016/j.jmmm.2019.166201
Resumen
In this work, a comparative study of the effect of Cu on the structural, magnetic and magnetic induction heating response in CdFe2O4 spinel is presented. The ceramic nanoparticles (Cu1−xCdxFe2O4; 0 ≤ x ≤ 1) were synthesized by co-precipitation from Cu(II), Cd(II) and Fe(III) salts. The samples, characterized by X-ray diffractometry, display the characteristic spinel cubic structure (space group F ...
[++]
In this work, a comparative study of the effect of Cu on the structural, magnetic and magnetic induction heating response in CdFe2O4 spinel is presented. The ceramic nanoparticles (Cu1−xCdxFe2O4; 0 ≤ x ≤ 1) were synthesized by co-precipitation from Cu(II), Cd(II) and Fe(III) salts. The samples, characterized by X-ray diffractometry, display the characteristic spinel cubic structure (space group Fm3m) where CdO is detected as main secondary phase (≈ 16% weight for x = 1). A high degree of nanoparticle agglomeration is inferred from the Transmission Electron Microscopy (TEM) images, as a consequence of the employed synthesis procedure. Regarding the magnetic properties, superparamagnetic behavior at room temperature can be disregarded according to the low field magnetization response (ZFC-FC curves). For 0.4 ≤ x ≤ 0.8 ratios, the samples display maximum values in the magnetic moment that should be correlated to the cation distribution between the octahedral and tetrahedral sites. Maximum magnetization values lead to an enhancement in the magnetic induction heating response characterized by highest heating temperatures under the action of an ac magnetic field. In particular, maximum SAR values are estimated for x = 0.8 as a combined effect of high magnetic moment, low dc coercive field (high susceptibility). Although these Cu-Cd ferrite nanoparticles display moderate SAR values (around 0.7 W/g), the control of the maximum heating temperatures through the cation distribution (composition) provides promising properties to be used as nanosized heating elements (i.e. hyperthermia agents). [--]
Materias
Magnetic nanoparticles,
Cd ferrites,
Cation distribution,
Magnetic hyperthermia
Editor
Elsevier
Publicado en
Journal of Magnetism and Magnetic Materials, 2020, 499, 166201
Departamento
Universidad Pública de Navarra. Departamento de Ciencias /
Nafarroako Unibertsitate Publikoa. Zientziak Saila /
Universidad Pública de Navarra/Nafarroako Unibertsitate Publikoa. Institute for Advanced Materials and Mathematics - INAMAT2
Versión del editor
Entidades Financiadoras
The work has been performed within the framework of projects MAT2017-83631-C3-2-R (Spanish 'Ministerio de Ciencia, Innovación y Universidades') and DRUG-MAG, Nueva generación de plataformas teragnósticas contra el cáncer asistidas por partículas superparamagnéticas (Gobierno de Navarra, Departamento de Desarrollo Económico). R. Ghasemi acknowledges the Iranian Ministry of Science, Research and Technology for the financial support at the Universidad Pública de Navarra.