Surface roughness influence on Néel-, crosstie, and Bloch-type charged zigzag magnetic domain walls in nanostructured Fe films
Fecha
2020Versión
Acceso abierto / Sarbide irekia
Tipo
Artículo / Artikulua
Versión
Versión publicada / Argitaratu den bertsioa
Impacto
|
10.3390/MA13194249
Resumen
Charged magnetic domain walls have been visualized in soft magnetic nanostructured Fe thin films under both static and dynamic conditions. A transition in the core of these zigzagged magnetic walls from Néel-type to Bloch-type through the formation of crosstie walls has been observed. This transition in charged zigzagged walls was not previously shown experimentally in Fe thin films. For film thi ...
[++]
Charged magnetic domain walls have been visualized in soft magnetic nanostructured Fe thin films under both static and dynamic conditions. A transition in the core of these zigzagged magnetic walls from Néel-type to Bloch-type through the formation of crosstie walls has been observed. This transition in charged zigzagged walls was not previously shown experimentally in Fe thin films. For film thicknesses t < 30 nm, Néel-type cores are present, while at t ≈ 33 nm, walls with crosstie cores are observed. At t > 60 nm, Bloch-type cores are observed. Along with the visualization of these critical parameters, the dependence on the film thickness of the characteristic angle and length of the segments of the zigzagged walls has been observed and analyzed. After measuring the bistable magneto-optical behavior, the values of the wall nucleation magnetic field and the surface roughness of the films, an energetic fit to these nucleation values is presented. [--]
Materias
Charged domain walls,
Magnetic thin films,
Magnetic wall energy,
Magneto-optic,
Pulsed laser deposition (PLD),
Roughness energy,
Scanning tunneling microscopy (STM)
Editor
MDPI
Publicado en
Materials, 2020, 13, 4249
Departamento
Universidad Pública de Navarra. Departamento de Ciencias /
Nafarroako Unibertsitate Publikoa. Zientziak Saila /
Universidad Pública de Navarra/Nafarroako Unibertsitate Publikoa. Institute for Advanced Materials and Mathematics - INAMAT2
Versión del editor
Entidades Financiadoras
The authors acknowledge the financial support from the Public University of Navarre, through the project PRO-UPNA18 (6105) and the grants 'Plan de Promoción Grupos de Investigación PPG/2019 and PPG/2020'.