Evaluation of the photocatalytic activity and anticorrosion performance of electrospun fibers doped with metallic oxides
Fecha
2021Versión
Acceso abierto / Sarbide irekia
Tipo
Artículo / Artikulua
Versión
Versión publicada / Argitaratu den bertsioa
Impacto
|
10.3390/polym13122011
Resumen
This paper reports the development and characterization of a multifunctional coating that combines anticorrosion and photocatalytic properties, deposited by means of the electrospinning technique. In the first step, a functional electrospun fiber mat composed of poly(acrylic acid) (PAA) and β-cyclodextrin (β-CD) was obtained, showing high water insolubility and great adhesion increased by means o ...
[++]
This paper reports the development and characterization of a multifunctional coating that combines anticorrosion and photocatalytic properties, deposited by means of the electrospinning technique. In the first step, a functional electrospun fiber mat composed of poly(acrylic acid) (PAA) and β-cyclodextrin (β-CD) was obtained, showing high water insolubility and great adhesion increased by means of a thermal crosslinking process (denoted as PAA + β-CD). In the second step, the fibers were doped with particles of titanium dioxide (denoted as PAA + β-CD/TiO2) and titanium dioxide plus iron oxide (denoted as PAA + β-CD/TiO2/Fe2O3). The morphology and fiber diameter of the electrospun mats were evaluated by using confocal microscopy, whereas the presence of the metal oxides in the electrospun fibers was corroborated by scanning electron microscopy (SEM) and X-ray fluorescence (XRF), respectively. In addition, electrochemical tests in saline solution revealed that the sample composed of PAA + β-CD/TiO2/Fe2O3 showed the highest corrosion protection efficiency of all the samples, which was directly associated to lower corrosion current density and higher corrosion potential. Furthermore, the paper reports a novel approach to in situ determination of methylene blue (MB) degradation onto the coating. The results revealed complete degradation of MB, which is perfectly appreciated by total discoloration of the film in the irradiated zone (from bluish to a white spot). The main conclusions of this research are the efficiency of the electrospun system PAA + β-CD/TiO2/Fe2O3 for developing photocatalytic activity and corrosion protection and the utility of the dry MB discoloration tests to evaluate photocatalytic activity. [--]
Materias
Corrosion protection,
Electrospun fiber mat,
Photocatalytic activity testing,
Polyacrylic acid (PAA),
Thermal crosslink,
β-cyclodextrin (β-CD)
Editor
MDPI
Publicado en
Polymers, 13 (12)
Departamento
Universidad Pública de Navarra. Departamento de Ingeniería /
Nafarroako Unibertsitate Publikoa. Ingeniaritza Saila /
Universidad Pública de Navarra/Nafarroako Unibertsitate Publikoa. Institute for Advanced Materials and Mathematics - INAMAT2
Versión del editor
Entidades Financiadoras
This research was funded by the Government of Navarra-Department of Economic Development (Project ARGITU) and by the Public University of Navarre (Project PJUPNA1929).