Influence of metallic die temperature in the solidification of Cu-10%Al-2%Fe alloy

The phases obtained in copper aluminium bronze alloy (Cu-Al10-Fe2) cast into a permanent die were investigated. The parameters examined were the pre-heating temperatures of the die and the graphite coating thickness. The phases α and γ2 were detected as well as the metastable phases β’ and γ’. The intermetallics of the system Fe-Al were obtained in various stoichiometric compositions. The different cooling rates of the casting resulted in two mechanisms of transformation to α grains out of the unstable β phase, one being nucleation and growth producing needle shaped α grains, the other exhibiting a massive transformation to spherical α grains. These two mechanisms determine the changes in the size of the α grains as a result of changes in the cooling rate in its various ranges.