M(II)-Al-Fe layered double hydroxides synthesized from aluminum saline slag wastes and catalytic performance on cyclooctene oxidation

Abstract

Aluminum was extracted from saline slags via an alkaline method and employed in the synthesis of Layered Double Hydroxides (LDH) with various M2+ cations (Co, Mg, Ni and Zn), while Al and Fe were the M3+ cations, using the co-precipitation method and a M2+/M3+ 2:1 ratio. The structural characterization of the samples was performed with powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), nitrogen physisorption at 77 K, thermogravimetric analysis (TGA), temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS). Their catalytic performance was tested for the oxidation of olefins (cyclooctene) and their biomimetic potential was analyzed. Results show a great selectivity towards epoxides with no other products obtained. Reaction yields followed the descending order Co4AlFe, Zn4AlFe, Ni4AlFe, and Mg4AlFe, the sample with cobalt as M2+ converting up to 85% of cyclooctene.