Development of ceramic-MOF filters from aluminum saline slags for capturing CO2

This study describes the procedures followed to synthesize ceramic-MOF filters using aluminum saline slag wastes. Briefly, the raw aluminum saline slags were washed at 80 ◦C to significantly reduce the saline content and eliminate gases. The pretreated material was mixed with glucose (G/S ratios between 0.2 and 1.6) and acetone by stirring for 4 h. After this time, the resulting solid was dried at 60 ◦C and then at 190 ◦C. During the glucose caramelization step, PegMn400 was also added and the temperature increased to 1200 ◦C. The obtained solid was impregnated with precursor solutions to achieve a supported ZIF-8 MOF. The ceramic-MOF filters were characterized by X-ray diffraction (XRD), N2 adsorption at 77 K, X-ray fluorescence (XRF), scanning electron microscopy (SEM) and transmission electron microscopy (HR-TEM), thereby confirming the presence of a structure that allows dispersion of the synthesized and supported ZIF-8. Finally, the performance of these ceramic-MOF filters as CO2 adsorbents was evaluated in the temperature range 50–300 ◦C, with isosteric heats of 19 kJ/mol being obtained using the Clausius-Clapeyron equation.