Publication: M(II)-Al-Fe layered double hydroxides synthesized from aluminum saline slag wastes and catalytic performance on cyclooctene oxidation
Consultable a partir de
Date
Authors
Director
Publisher
Project identifier
Abstract
Aluminum was extracted from saline slags via an alkaline method and employed in the synthesis of Layered Double Hydroxides (LDH) with various M2+ cations (Co, Mg, Ni and Zn), while Al and Fe were the M3+ cations, using the co-precipitation method and a M2+/M3+ 2:1 ratio. The structural characterization of the samples was performed with powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), nitrogen physisorption at 77 K, thermogravimetric analysis (TGA), temperature-programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS). Their catalytic performance was tested for the oxidation of olefins (cyclooctene) and their biomimetic potential was analyzed. Results show a great selectivity towards epoxides with no other products obtained. Reaction yields followed the descending order Co4AlFe, Zn4AlFe, Ni4AlFe, and Mg4AlFe, the sample with cobalt as M2+ converting up to 85% of cyclooctene.
Keywords
Department
Faculty/School
Degree
Doctorate program
Editor version
Funding entities
© 2022 The Author(s). This is an open access article under the CC BY-NC-ND license
Los documentos de Academica-e están protegidos por derechos de autor con todos los derechos reservados, a no ser que se indique lo contrario.